Tati Karliati, . and Fauzi Febrianto, . and Wasrin Syafii, . and Mohd. Hamami Sahri, . (2006) Gutta percha Palaquium oblongifolium resin as a hot melt adhesive. [Proceedings Paper]

Modification of Gutta percha Palaquium oblongifolium resin natural trans-1 4-isoprene rubber TIR Guta percha with 5 maleic anhydride MAH was done in the kneader Toyo Seiki Labo-Plastomill. The resulted product MAH-modified-TIR so called MTIR was used as adhesive for plywood manufacturing. The veneer used was Keruing wood Dipterocarpus spp with the moisture content in the range of 4-6. The MTIR veneer and plywood properties under various glue spreads ranging from 175 to 250g/m2 were evaluated. In the spectrum of MTIR after purification in which unreacted of MAH was removed the peak at 1716cm-1 existed indicated the characteristic for C0 of MAH. Differential thermal analysis showed that before and after modification the melting and the decomposition temperature of TIR Gutta percha was quite different indicate that chemical modification of TIR Gutta percha with MAH occured.Modification of TIR Gutta percha with MAH resulted in improvement of the plywood quality i.e increasing the shear strength and wood failure values.MTIR prepared from both TIR Gutta percha is thermoplastics like and can be used as interior and exterior plywood adhesive.

Full text available from:

Abstract

Modification of Gutta percha Palaquium oblongifolium resin natural trans-1 4-isoprene rubber TIR Guta percha with 5 maleic anhydride MAH was done in the kneader Toyo Seiki Labo-Plastomill. The resulted product MAH-modified-TIR so called MTIR was used as adhesive for plywood manufacturing. The veneer used was Keruing wood Dipterocarpus spp with the moisture content in the range of 4-6. The MTIR veneer and plywood properties under various glue spreads ranging from 175 to 250g/m2 were evaluated. In the spectrum of MTIR after purification in which unreacted of MAH was removed the peak at 1716cm-1 existed indicated the characteristic for C0 of MAH. Differential thermal analysis showed that before and after modification the melting and the decomposition temperature of TIR Gutta percha was quite different indicate that chemical modification of TIR Gutta percha with MAH occured.Modification of TIR Gutta percha with MAH resulted in improvement of the plywood quality i.e increasing the shear strength and wood failure values.MTIR prepared from both TIR Gutta percha is thermoplastics like and can be used as interior and exterior plywood adhesive.

[error in script]

Item Type:	Proceedings Paper
Additional Information:	3 ills. 3 tables. 18 refs.
AGROVOC Term:	GUTTA-PERCHA
AGROVOC Term:	PALAQUIUM
AGROVOC Term:	MH
AGROVOC Term:	GROWTH INHIBITORS
AGROVOC Term:	ADHESIVES
AGROVOC Term:	PLYWOOD
Geographical Term:	MALAYSIA
Depositing User:	Ms. Norfaezah Khomsan
Last Modified:	24 Apr 2025 05:28
URI:	http://webagris.upm.edu.my/id/eprint/16954

Actions (login required)

View Item